Page 805
... resin and dimethylamine mixture under the same conditions took about 30 minutes to harden . The mixture of Epon 828 and Dicy showed no signs of hardening even with prolonged heating at 116 ° C . The 20 experiments of the study are ...
... resin and dimethylamine mixture under the same conditions took about 30 minutes to harden . The mixture of Epon 828 and Dicy showed no signs of hardening even with prolonged heating at 116 ° C . The 20 experiments of the study are ...
Page 813
... Resins The modified resins have a lower curing temperature . Imide monomers can be chemically modified to lower their cure temperature by 90 ° , at the least , without compromising the flame resistance of the cured resins made from them ...
... Resins The modified resins have a lower curing temperature . Imide monomers can be chemically modified to lower their cure temperature by 90 ° , at the least , without compromising the flame resistance of the cured resins made from them ...
Page 815
... resin , and triethylenetetramine curing agent , with the mixture containing about 85 percent silica and aggregate particles and 15 percent resin and curing agent . The silica is a thickening agent and keeps the grout from sagging . The ...
... resin , and triethylenetetramine curing agent , with the mixture containing about 85 percent silica and aggregate particles and 15 percent resin and curing agent . The silica is a thickening agent and keeps the grout from sagging . The ...
Common terms and phrases
1984 Filing Code 5285 Port Royal ADDITIONAL INFORMATION Aeronautics and Space alloys alumina aluminum ARMY MATERIEL DEVELOPMENT ARTICLE assumes any liability Autofrettage BWI Airport Caltech for NASA's Contact crack growth DEVELOPMENT AND READINESS dimethylamine Directorate for Manufacturing document was prepared ELECTRICAL RESISTIVITY fact sheet ferroelectric fibers free from privately glass ceramics Government assumes grout Information Service 5285 isopropyl alcohol Jet Propulsion Laboratory Johnson Space Center JUNE 1984 Filing Lawrence Berkeley Laboratory learn more details liability resulting loading Manufacturing Technology Martensitic melter metal NASA's Jet Propulsion National Technical Information NTIS report(s NUMBER LISTED Order number ordering the NTIS P.O. Box percent overstrain porosity Port Royal Rd Price code privately owned rights pyroelectric READINESS COMMAND Directorate rhenium Service 5285 Port silane sintered Springfield Tech Notes Technical Information Service technology by ordering Technology Transfer Division Tensile Strength tested U.S. ARMY MATERIEL U.S. DEPARTMENT U.S. Government United States Government Virginia Project Number