Tech Notes: MaterialsNational Technical Information Service., 1984 - Manufacturing processes |
From inside the book
Results 1-3 of 3
Page 805
... Curing of Epoxy Resins Trisubstituted urea / epoxy mixture generates amine that lowers the curing temperature . D This document was prepared under the sponsorship of the U.S. Government . Neither the United States Government nor any ...
... Curing of Epoxy Resins Trisubstituted urea / epoxy mixture generates amine that lowers the curing temperature . D This document was prepared under the sponsorship of the U.S. Government . Neither the United States Government nor any ...
Page 813
... Cured imide resins and composites with high heat and flame resistances are obtained by heating the imide monomers or graphite fibers impregnated with them to curing temperatures of 180 ° C and postcuring temperatures of 220 ° C . This ...
... Cured imide resins and composites with high heat and flame resistances are obtained by heating the imide monomers or graphite fibers impregnated with them to curing temperatures of 180 ° C and postcuring temperatures of 220 ° C . This ...
Page 815
... curing in the presence of hydraulic oil . The grout is a mixture of aggregate particles , finely - divided silica , epoxy resin , and triethylenetetramine curing agent , with the mixture containing about 85 percent silica and aggregate ...
... curing in the presence of hydraulic oil . The grout is a mixture of aggregate particles , finely - divided silica , epoxy resin , and triethylenetetramine curing agent , with the mixture containing about 85 percent silica and aggregate ...
Common terms and phrases
1984 Filing Code 5285 Port Royal ADDITIONAL INFORMATION Aeronautics and Space alloys alumina aluminum ARMY MATERIEL DEVELOPMENT ARTICLE assumes any liability Autofrettage BWI Airport Caltech for NASA's Contact crack growth DEVELOPMENT AND READINESS dimethylamine Directorate for Manufacturing document was prepared ELECTRICAL RESISTIVITY fact sheet ferroelectric fibers free from privately glass ceramics Government assumes grout Information Service 5285 isopropyl alcohol Jet Propulsion Laboratory Johnson Space Center JUNE 1984 Filing Lawrence Berkeley Laboratory learn more details liability resulting loading Manufacturing Technology Martensitic melter metal NASA's Jet Propulsion National Technical Information NTIS report(s NUMBER LISTED Order number ordering the NTIS P.O. Box percent overstrain porosity Port Royal Rd Price code privately owned rights pyroelectric READINESS COMMAND Directorate rhenium Service 5285 Port silane sintered Springfield Tech Notes Technical Information Service technology by ordering Technology Transfer Division Tensile Strength tested U.S. ARMY MATERIEL U.S. DEPARTMENT U.S. Government United States Government Virginia Project Number